Adesão do Selante Clinpro™ XT à Superfície Oclusal de Molares Decíduos: Avaliação Longitudinal / Clinpro ™ XT Sealant Adhesion to the Occlusal Surface of Primary Molars: Longitudinal Evaluation

The study aims to evaluate the bond strength of sealants on deciduous molars. Clinpro ™ XT, Vitremer ™, Fluroshield and Optibond FL materials were applied to the occlusal surface of 40 deciduous lower molars (n = 5). The teeth were prepared for the micro tensile test, obtaining a specimen in a stick format with a cross-sectional area of 0.8 mm2 . After 24 hours and 6 months of restorative procedures, the specimens were traversed in universal test machine. The statistical analysis used the tooth as experimental unit, considering the adhesive and mixed fractures data, through Variance Analysis of repeated measures and Tukey tests (α = 0.05). There was a difference among the adhesion of the materials in 24 h, with higher union strength for Optibond FL (31.20 ± 1.36 MPa), significantly higher than that of Clinpro ™ XT (20.23 ± 1.16 MPa), Fluroshield (24.61 ± 2.76 MPa) and Vitremer™ (21.31 ± 2.32 MPa), which were similar. After 6 months of storage, the Clinpro ™ XT bond strength remained (22.18 ± 2.91 MPa), Optibond FL decreased (20.77 ± 1.53 MPa), but remained similar to that of Clinpro ™ XT in 6 months. The lowest adhesion values at 6 months were of Fluroshield (11.14 ± 1.98 Mpa) and Vitremer (5.29 ± 0.58 Mpa). It was concluded that the bond strength of the sealants to the occlusal surface of the deciduous molars was influenced by the material, with Clinpro ™ XT being the only material that maintained the bond strength values after 6 months. (AU).

O presente estudo teve como objetivo avaliar a adesão de selantes em molares decíduos. Os materiais Clinpro™ XT, VitremerTM, Fluroshield e Optibond FL foram aplicados na superfície oclusal de 40 molares inferiores decíduos (n=5). Os dentes foram preparados para o ensaio de microtração, com obtenção de corpo-de-prova em formato de palito com área de seção transversal de 0,8 mm2 . Após 24 horas e 6 meses da realização dos procedimentos restauradores, os espécimes foram tracionados em máquina de ensaio universal. A análise estatística usou como unidade experimental o dente, considerando os dados de fraturas adesivas e mistas, pelos testes de Análise de Variância de medidas repetidas e Tukey (α=0,05). Houve diferença entre a adesão dos materiais em 24 h, com maior resistência de união para o Optibond FL (31,20 ±1,36 MPa), significativamente maior que a do Clinpro™ XT (20,23 ±1,16 MPa); Fluroshield (24,61 ±2,76 MPa) e VitremerTM (21,31 ±2,32 MPa) foram semelhantes. Decorridos 6 meses de armazenamento, a resistência de união do Clinpro™ XT se manteve (22,18 ±2,91 MPa) e a do Optibond FL diminuiu (20,77 ±1,53 MPa) mas se manteve semelhante à do Clinpro™ XT em 6 meses. Os menores valores de adesão em 6 meses foram do Fluroshield (11,14 ±1,98 Mpa) e do Vitremer (5,29 ±0,58 Mpa). Concluiu-se que a resistência de união dos selantes à superfície oclusal dos molares decíduos foi influenciada pelo material, sendo o Clinpro™ XT o único material que manteve os valores de resistência de união após 6 meses. (AU).

Bonding durability of dental sealants to deciduous and permanent teeth

AIM: To evaluate the bonding durability of materials used as sealants on different dentitions. METHODS: Deciduous (D) and permanent (P) molars were divided into four groups (n=5) and sealed with Fluroshield (F) and OptiBond FL (FL). Blocks of composite resin were built, stored in distilled water (24 h/37 °C), sectioned into 0.8 mm2 and tested at tensile (0.5 mm/min) after 24 h and 6 months. The fractures were observed and classified into adhesive, cohesive or mixed types. The data were analyzed using repeated measures ANOVA and Tukey test (α=5%), with tooth as the experimental unit. RESULTS: There were differences for dentition (p=0.0097), dental sealant (p=0.0019) and time (p=0.0001). At 24h the highest bond strength was observed for OptiBond FL on deciduous and permanent teeth, similar to Fluroshield at both dentitions. After 6 months the bond strength of OptiBond FL did not decrease in the permanent teeth, but decreased similar to Fluroshield in deciduous teeth, the bond strength of Fluroshield decreased similarly in both dentitions. CONCLUSIONS: The bond strength of dental sealants varied with the experimental conditions...

Oral health promotion in early childhood: age of joining preventive program and behavioral aspects / Promoção da saúde oral na primeira infância: idade de ingresso em programas preventivos e aspectos comportamentais / Promoção da saúde oral na primeira infância: idade de ingresso em programas preventivos e aspectos comportamentais

Objective : To analyze the interference of age in the entrance into a public dental care program for infants as well as family behavioral aspects about tooth decay experience in children 0 to 4 years old. Methods : Cross-sectional study involving 465 children who were divided into 3 groups: infants whose mothers joined the program during pregnancy (n=50); infants enrolled in the program during the first year of life (n=230); and infants enrolled in the program between 13 and 18 months old (n=185). The χ2 and Kruskal-Walis tests (95% confidence interval) were used to assess the relationship among variables. Results : There was an association between the age of entrance in the programs and dental caries (p<0.001). A lower prevalence was seen in infants whose mothers joined the program during pregnancy, and among those infants enrolled in the program during the first year of life. The same low prevalence occurred in relation to mothers’ commitment to attend follow-up visits with their infants, cariogenic diet, nighttime oral care, duration of night feeding and parents’ educational level (p<0.001). Unfavorable socioeconomic conditions (p>0.05) and daily oral care (p=0.214) were common variables in the groups with 99% of occurrence. Commitment to attend follow-up visits, nighttime oral care and parents’ educational level (p>0.05) were considered protective factors for dental caries. Cariogenic diet and night feeding were determinant factors to the appearance of dental caries. Conclusion : To promote children oral health it is essential to enroll children in oral health programs and adopt healthy habits as early as possible, besides the adherence of the child to their parents’ advice. .

Objetivo : Analisar a interferência da idade de ingresso em programas públicos de Odontologia para crianças e dos aspectos comportamentais familiares sobre a experiência com cárie dentária em crianças de zero a 48 meses de idade. Métodos : Estudo transversal com 465 crianças divididas em 3 grupos: crianças cujas mães ingressaram no programa quando gestantes (n=50); crianças que ingressaram no programa durante o primeiro ano de vida (n=230); e crianças que ingressaram no programa entre 13 e 18 meses de idade (n=185). Os testes χ2 e Kruskal-Walis (intervalo de confiança de 95%) foram utilizados para avaliar a relação das variáveis. Resultados : Encontrou-se associação entre a idade do ingresso nos programas e cárie dentária (p<0,001), sendo menor a prevalência para crianças cuja as mães ingressaram no programa durante as gestação e para aqueles que ingressaram no programa durante o primeiro ano de vida, o mesmo ocorreu em relação a assiduidade as consultas de retorno, dieta cariogênica, higiene oral noturna, duração de aleitamento noturno e escolaridade materna/responsável (p<0,001). Desfavorável nível socioeconômico (p>0,05) e higiene oral diária (p=0,214) foram variáveis comuns nos grupos com 99% de ocorrência. Assiduidade, higiene oral noturna e escolaridade materna (p<0,05) foram consideradas fatores de proteção à cárie dentária. Dieta cariogênica e aleitamento noturno foram consideradas determinantes para o aparecimento da cárie dentária. Conclusão : Para promover saúde oral infantil é essencial o ingresso ao programa e adoção de hábitos saudáveis de maneira precoce, além da adesão às orientações por seus responsáveis. .

Dentistry for babies: caries experience vs. assiduity in clinical care

Aim: This study analyzed and compared the experience of dental caries in 300 children aged 0 to 48 months, who were participants and non-participants of a preventive program ‘Dentistry for babies’, as well as the correlation between assiduity of dental visits and experience of dental caries. Methods: The subjects were randomly selected and divided into two groups: G1 ‘Nonparticipant children of the Program’ (n=100) and G2 ‘Participant Children of the Program’ (n=200). Each group was subdivided in two subgroups: 0-24 months and 25-48 months. The collecteddata from G2 were analyzed, relating the variation of the dmft index (dmft refers to primary teeth: d = decayed, m = missing/extracted due to caries, f = filled, t = teeth) (C) and dental caries prevalence (P) with the influence of assiduity factor in each subgroup. To collect data, clinical examinations were performed using tactile and visual criteria by a single calibrated examiner.The data were statistically analyzed using the ‘paired t-test’, ‘Mann-Whitney’ and ’Chi-Squared’ tests (p<0.05). Results: It was found that prevalence and dmft index were statistically significant (P=0.0001) with the greatest values observed in G1 (p=0.0001). The values were: PG1 (73%), PG2 (22%), CG1 (3.45±3.84), CG2 (0.66±1.57). Assiduity was significant in G2 (p=0.0001). The values observed were: P-Assiduous (2%), P-Non-assiduous (42%), C-Assiduous (0.04±0.31), and C-Non-assiduous (1.29±2.01). Conclusions: The participation in the program had a positive influence on the oral health of babies. Complete assiduity to the program resulted in the lowest rates and prevalence of dental caries.

Cariogenicidade do leite materno: mito ou evidência científica / Human milk cariogenicity: myth or scientific evidence

Introdução:A amamentação materna tem sido destacada como medida de promoção de saúde, fazendo parte da Política Nacional de Saúde, envolvendo o profissional da Odontologia, porém o leite materno tem sido sugerido como um fator de risco para o desenvolvimento da cárie precoce da infância. Objetivo: Buscar evidências científicas na literatura que comprovem ou refutem a afirmação de que o aleitamento materno está associado com a Cárie Precoce da Infância. Método: A partir da consulta das bases de dados Medline e SciELO, foram incluídos desde estudos laboratoriais a levantamentos epidemiológicos que relacionam o aleitamento materno com a presença da doença cárie. Os descritores utilizados para esta busca foram: "breast feeding" e "dental caries". Constatou-se que não existem evidências científicas adequadas que demonstrem relação clara sobre a cariogenicidade do leite materno, em virtude da doença cárie ser multifatorial, o que a torna susceptível a presença de fatores confundidores, como por exemplo, a introdução precoce da sacarose a dieta do lactente e o início tardio de hábitos de higiene bucal. O aleitamento materno exclusivo deve ser estimulado pelo cirurgião dentista, uma vez que, além dos inegáveis benefícios para a saúde física e psicológica da criança, favorece um crescimento facial harmônico e previne o desenvolvimento de deglutição atípica e de maloclusões, em conjunto com a inserção precoce de hábitos de higiene e dieta não cariogênica. Conclusão: Não existem evidências científicas que suportem a afirmação de que o aleitamento materno está associado com a Cárie Precoce da Infância.

Introduction: Breast-feeding has stood out as health care measure and is part of the Government's National Health Policy, involving dental professionals. However, it has been suggested that breast milk could be a risk factor for the development of early childhood caries. Objective: The purpose of this report was to search for scientific evidence that would support or refute the statement that breastfeeding is associated with the development of early childhood caries. Method: Medline and SciELO databases were consulted to retrieve studies, ranging from laboratory investigations to epidemiological surveys, which relate breastfeeding to dental caries. The key words 'breast-feeding' and 'dental caries' were used on the reference search. There was no scientific evidence that could demonstrate a clear relationship between breast milk and cariogenicity. This is attributed to fact that dental caries is a multifactorial disease that is susceptible to multiple confusing factors, among which the early introduction of sucrose to the infant's diet and late introduction of oral hygiene habits. The dentist should encourage exclusive breast-feeding because, in addition to the undeniable benefits to the child's physical and psychological health, it contributes to a harmonic facial growth and prevents the development of atypical deglutition and malocclusions, in combination with early introduction of oral hygiene habits and noncariogenic diet. Conclusion: There is no scientific evidence to demonstrate an association between breast-feeding and early childhood caries.

Experiência de cárie dentária em crianças atendidas em um programa de Odontologia para bebês / Dental caries in children participating in a Dentistry for infants program

Objective: To assess the impact of the "Dentistry for Infants" early dental care program run by Jacareí County (SP) by comparing the caries of individuals participating and not participating in this program. Methods: In total, 300 children between 0 and 48 months old were assessed in the following two groups: infants not participating in the program (G1, n = 100) and infants participating in the program (G2, n = 200). Each group was further divided according to age in subgroups of 0 to 24 months and 25 to 48 months. All children were clinically assessed for carious lesions using the visual-tactile method. The data were statistically analyzed using a paired Student's t-test, Mann-Whitney test, and X² test at a 5% significance level. Results: There was a significant difference in the prevalence (P) and mean index of deciduous teeth (deft) (C) that were decayed, indicated for extraction and filled, and the highest values were observed in G1 (p < 0.0001). The values were as follows: PG1, 73%; PG2, 22%; CG1, 3.45 ± 3.84; and CG2, 0.66 ± 1.57. Conclusion: Participating in the program positively impacted the infants' oral health.

Objetivo: Avaliar o impacto na saúde bucal de crianças atendidas em um programa de atenção precoce "Odontologia para Bebês" da prefeitura do município de Jacareí (SP), por meio da comparação da experiência de cárie entre indivíduos participantes e não participantes do programa. Métodos: Foram avaliadas 300 crianças de 0 e 48 meses de idade, as quais foram divididas em 2 grupos: G1"Bebês não participantes do Programa" (n = 100) e G2 "Bebês do Programa" (n = 200). Cada grupo foi subdividido em dois, o primeiro com crianças de 0 a 24 meses, e o segundo de 25 a 48 meses. Todas as crianças receberam avaliação clínica quanto à presença de lesões de cárie (método táctil e visual). Os dados foram tabulados e analisados estatisticamente pelos testes t de Student pareado, Mann-Whitney e X², com nível de significância de 5%. Resultados: Houve diferença estatística para a prevalência (P) e o índice médio de dentes decíduos cariados, com extração indicada e obturados (ceod) (C), sendo os maiores valores observados para G1(p < 0,0001). Os valores foram: PG1 (73%), PG2 (22%), CG1 (3,45 ± 3,84), CG2 (0,66 ± 1,57). Conclusão: Concluiu-se que participar do programa interferiu positivamente na saúde bucal dos bebês.

Microhardness of glass ionomer cements indicated for the ART technique according to surface protection treatment and storage time

The aim of this study was to assess the microhardness of 5 glass ionomer cements (GIC) - Vidrion R (V, SS White), Fuji IX (F, GC Corp.), Magic Glass ART (MG, Vigodent), Maxxion R (MR, FGM) and ChemFlex (CF, Dentsply) - in the presence or absence of a surface protection treatment, and after different storage periods. For each GIC, 36 test specimens were made, divided into 3 groups according to the surface protection treatment applied - no protection, varnish or nail varnish. The specimens were stored in distilled water for 24 h, 7 and 30 days and the microhardness tests were performed at these times. The data obtained were submitted to the ANOVA for repeated measures and Tukey tests (á = 5 percent). The results revealed that the mean microhardness values of the GICs were, in decreasing order, as follows: F > CF = MR > MG > V; that surface protection was significant for MR, at 24 h, without protection (64.2 ± 3.6a), protected with GIC varnish (59.6 ± 3.4b) and protected with nail varnish (62.7 ± 2.8ab); for F, at 7 days, without protection (97.8 ± 3.7ab), protected with varnish (95.9 ± 3.2b) and protected with nail varnish (100.8 ± 3.4a); and at 30 days, for F, without protection (98.8 ± 2.6b), protected with varnish (103.3 ± 4.4a) and protected with nail varnish (101 ± 4.1ab) and, for V, without protection (46 ± 1.3b), protected with varnish (49.6 ± 1.7ab) and protected with nail varnish (51.1 ± 2.6a). The increase in storage time produced an increase in microhardness. It was concluded that the different GICs, surface protection treatments and storage times could alter the microhardness values.

Influência do Fator Assiduidade à Consulta Odontológica na Prevalência de Cárie Dentária em Indivíduos Atendidos na BebêClínica da Prefeitura do Município de Jacareí, SP, Brasil / Influence of the Assiduity to Dental Consultations on the Prevalence of Caries Disease in Children Treated at the Municipal Baby Clinic in the City of Jacareí, SP, Brazil

Objetivo: Avaliar a influência do fator assiduidade à consultaodontológica no atendimento à bebês.Método: Foram avaliadas 100 crianças, na faixa etária entre 0 e48 meses, que freqüentaram a Bebê Clínica da Prefeitura Municipalde Jacareí, São Paulo. Estas foram divididas em 2 grupos: G1(n=50): Bebês assíduos ao programa, ou seja, sem nenhuma faltanas rechamadas; G2 (n=50): Bebês não assíduos ao programa, ouseja, com pelo menos uma falta não justificada. Todas as criançasreceberam avaliação clínica quanto à presença de lesões de cárie(método táctil e visual), com uso de sonda exploradora e espelhoclínico. Os dados foram tabulados e analisados estatisticamentepelo Teste T-Student (p=0,001), do Programa Minitab versão 14.12(2004).Resultados: As crianças do grupo assíduo (G1) apresentaramum ceo-d médio de 0,4 (±1,58), enquanto que as crianças do gruponão assíduo (G2) apresentaram um ceo-d médio de 3,6 (±3,14). Aanálise estatística indicou que as crianças do grupo não assíduo(G2) apresentaram um ceo-d médio significantemente maior doque as crianças do grupo assíduo (G1).Conclusão: O fator assiduidade interferiu positivamente no nívelde saúde bucal das crianças atendidas na Bebê Clínica da Prefeiturado Município de Jacareí/SP, Brasil.

Bond strength of resin modified glass ionomer cement to primary dentin after cutting with different bur types and dentin conditioning

The aim of this in vitro study was to evaluate the effect of different bur types and acid etching protocols on the shear bond strength (SBS) of a resin modified glass ionomer cement (RM-GIC) to primary dentin. Forty-eight clinically sound human primary molars were selected and randomly assigned to four groups (n=12). In G1, the lingual surface of the teeth was cut with a carbide bur until a 2.0-mm-diameter dentin area was exposed, followed by the application of RM-GIC (Vitremer - 3M/ESPE) prepared according to the manufacturer's instructions. The specimens of G2, received the same treatment of G1, however the dentin was conditioned with phosphoric acid. In groups G3 and G4 the same procedures of G1 and G2 were conducted respectively, nevertheless dentin cutting was made with a diamond bur. The specimens were stored in distilled water at 37ºC for 24h, and then tested in a universal testing machine. SBS. data were submitted to 2-way ANOVA (= 5 percent) and indicated that SBS values of RM-GIC bonded to primary dentin cut with different burs were not statistically different, but the specimens that were conditioned with phosphoric acid presented SBS values significantly higher that those without conditioning. To observe micromorphologic characteristics of the effects of dentin surface cut by diamond or carbide rotary instruments and conditioners treatment, some specimens were examined by scanning electron microscopy. Smear layer was present in all specimens regardless of the type of rotary instrument used for dentin cutting, and specimens etched with phosphoric acid presented more effective removal of smear layer. It was concluded that SBS of a RM-GIC to primary dentin was affected by the acid conditioning but the bur type had no influence.

Micromorfologia da interface da união sistema restaurador-dentina decídua em função do sistema adesivo e do instrumento cortante rotatório / Micromorphology of the restorative system-primary dentin adhesive interface as a function of the adhesive system and rotary cutting instrument

Objetivo: Avaliar, in vitro a micromorfologia da interface da união sistema restaurador-dentina decídua, em função do sistema adesivo e do instrumento cortante rotatório. Método: Foram utilizados 20 segundos molares decíduos divididos aleatoriamente em dois grupos (n=10). No grupo C, foi realizado desgaste, até atingir a dentina, com ponta carbide. No grupo D, foi feito o mesmo desgaste, porém com ponta diamantada. A superfície preparada de cada dente foi dividida ao meio, sendo que em uma metade foi aplicado um sistema adesivo convencional de duas etapas (Single-Bond - 3M) e na outra um sistema autocondicionante de etapa única (One Up Bond F - Tokuyama). Todos os dentes foram restaurados com a resina composta híbrida (Filtek Z250 - 3M). As amostras foram termocicladas, embutidas em resina, seccionadas para obtenção da interface de união e preparadas para observação ao MEV. Resultados: Os dois sistemas adesivos utilizados foram capazes de formar camada híbrida. O sistema adesivo convencional de duas etapas proporcionou melhor selamento da interface de união, quando comparada ao autocondicionante e o emprego da ponta diamantada com o adesivo autocondicionante, mostrou o pior selamento da interface de união, com os maiores valores de gap. Conclusão: O instrumento cortante rotatório (ponta diamantada) só apresentou influência negativa na qualidade da interface sistema restaurador-dentina decídua quando se empregou sistema adesivo autocondicionante de etapa única.

Purpose: To evaluate, in vitro, the micromorphology of therestorative system-primary dentin interface as a function of theadhesive system and rotary cutting instrument.Method: Twenty primary second molars were randomly assignedto two groups (n=10). In group C, the teeth were ground with acarbide bur until reaching the dentin. In group D, the same procedurewas done however using a diamond bur. The prepared surface ofeach tooth was bisected. In one half, a 2-step total-etch adhesivesystem (Single-Bond - 3M) was applied and in the other half, a 1-step self-etching adhesive system (One Up Bond F - Tokuyama)was applied. All teeth were restored with a hybrid composite resin(Filtek Z250 - 3M). The specimens were thermocycled, embeddedin resin, sectioned to obtain the adhesive interface and preparedfor SEM analysis.Results: Both adhesive systems were capable of forming a hybridlayer. The 2-step total-etch adhesive system provided a bettersealing of the adhesive interface, in comparison to the self-etchingadhesive system. The use of a diamond bur together with the selfetchingadhesive system yielded the worst sealing of the adhesiveinterface, with presence of larger gaps.Conclusions: The rotary cutting instrument (diamond bur) had anegative influence on the quality of the restorative system-primarydentin interface only when a 1-step self-etching adhesive systemwas used.

Aspectos relacionados a procedimentos restauradores em odontopediatria / Aspects related to restorative procedures in pediatric dentistry

O objetivo deste texto foi realizar uma revisão crítica de trabalhos realizados após o doutoramento do autor, de parte de uma linha de pesquisa focalizada na dentística em odontopediatria. Desta forma, foram revisados artigos referentes a alguns procedimentos realizados na prática da odontologia restauradora, envolvendo estudos de microinfiltração, onde foi avaliada a influência de técnicas e materiais restauradores sobre este fenômeno. Outros trabalhos revisados relacionaram-se ao uso do microscópio eletrônico de varredura. Neste caso, foram descritos estudos que avaliaram aspectos micromorfológicos das estruturas dentárias (esmalte e dentina) de dentes permanentes, mas principalmente decíduos. Foram observados os efeitos de diferentes tratamentos realizados sobre as estruturas dentárias, como a ação de agentes condicionadores e métodos de desgaste das estruturas dentárias (laser, abrasão a ar, instrumentos cortantes rotatórios e ponta CVD). Também foram apresentados os trabalhos que avaliaram a interface adesiva, após diferentes tratamentos da dentina. Finalmente foram realizados comentários sobre os trabalhos revisados e apresentadas as tendências futuras desta linha de pesquisa.

Micromorfologia do esmalte decíduo intacto ou desgastado em função do agente condicionador / Micromorphology of grounded or ungrounded primary enamel in function of the etchant

O objetivo deste estudo foi observar, ao microscópio eletrônico de varredura (MEV), a micromorfologia do esmalte de dentes decíduos intacto ou desgastado após condicionamento com ácido fosfórico a 37% ou com sistemas adesivos autocondicionantes de uma ou duas etapas. Foram selecionados 15 dentes decíduos, que foram divididos em três grupos, com 5 dentes em cada, de acordo com o agente condicionador e dentre eles, sub-divididos mantendo-se a superfície do esmalte intacta ou desgastada. G1: ácido fosfórico a 37% (Condicionador Dental Gel - Dentsply). G1A: esmalte intacto. G1B: esmalte desgastado. G2: condicionamento com primer do sistema adesivo autocondicionante de duas etapas (Adhese - Ivoclar Vivadent). G2A: esmalte intacto. G2B: esmalte desgastado. G3: condicionamento com sistema adesivo autocondicionante de etapa única (Xeno III – Dentsply). G3A: esmalte intacto. G3B: esmalte desgastado. Após os tratamentos propostos, todas as amostras foram desidratadas, montadas em bases metálicas e observadas ao MEV quanto ao padrão de condicionamento ácido. As amostras do G1A revelaram um padrão não homogêneo de condicionamento (áreas de esmalte condicionado e outras não condicionadas). No G1B foi observado um padrão homogêneo de condicionamento, prevalecendo o padrão Tipo 2 de Silverstone et al.(1975). As amostras dos G2A e G2B não revelaram um padrão homogêneo de condicionamento, tanto no esmalte íntegro como no desgastado. Concluiu-se que o uso do ácido fosfórico parece ser mais favorável para a formação de uma superfície micro retentiva, notadamente no esmalte desgastado. O uso de sistemas adesivos autocondicionantes, tanto no esmalte intacto como no desgastado não propiciou a formação de uma superfície do esmalte micro retentiva.

The aim of this study was to examinate under scanning electron microscopy (SEM) the micromorphology of grounded and ungrounded primary enamel after conditioning with 37% phosphoric acid, single or two-step self etching adhesive systems. Fiftheen primary teeth were selected and divided into three groups (n=5), according to the etchant and then sub-divided maintaining the enamel surface ungrounded or grounded. G1: 37% phosphoric acid (Condicionador Dental Gel – Dentsply). G1A: ungrounded enamel. G1B; grounded enamel. G2: etching with primer of a two-step adhesive system Adhese (Ivoclar – Vivadent). G2A: ungrounded enamel. G2B: grounded enamel.G3: etching with a single-step adhesive system (Xeno III – Dentsply). G3A: ungrounded enamel. G3B: grounded enamel. After enamel etching, all the samples were dehydrated, mounted on metal stubs and observed by SEM for etching pattern. G1A samples showed a non-uniform pattern of enamel etching (with etched and unetched areas). In G1B samples it was observed an uniform Type 2 etching pattern, according Silverstone et al. (1975). G2A and G2B samples did not reveal an uniform etching pattern, for both grounded and ungrounded enamel. It was concluded that the use of phosphoric acid seems to be more suitable to create a micro retentive surface, specially when enamel surface was grounded. Use of a self etching adhesive system on grounded or ungrounded primary enamel did not propitiate the formation of a microretentive enamel pattern.

Efeito da microabrasão sobre mancha branca de carie inativa em dentes decíduos / Effects of microabrasion on non active white spots in primary teeth

Observar a micromorfologia do esmalte de dentes decíduos com lesão de mancha branca de cárie inativa, após aplicação de dois diferentes compostos indicados para a técnica da microabrasão. Método: Foram selecionados 30 molares decíduos que apresentavam lesões de manchas brancas de cárie inativa nas faces proximais, divididos aleatoriamente em três grupos. G1 (n=10): grupo controle, sem tratamento. G2 (n=10): aplicação do composto de gel de ácido fosfórico a 35 por cento e pedra-pomes extrafina (1:1), sobre a superfície do esmalte dentário manchado. G3 (n=10): aplicação do Opalustre (Ultradent), composto de ácido clorídrico a 6,6 por cento e micropartículas de carbureto de silício em pasta solúvel emágua. A seguir, as amostras foram desidratadas, montadas em bases metálicas e cobertas com ouro para observação ao microscópio eletrônico de varredura. Resultados: Asobservações das eletromicrografias revelaram que as amostras do G1 apresentaram-se lisas com a presença de restos de pedra-pomes. No G2 os espécimes revelaram-se rugosos e apresentando áreas de desmineralização dos prismas do esmalte. Já no G3, foi observada a formação de riscos e ranhuras, além da presença de restos do composto abrasivo. Conclusão: A aplicação de diferentes compostos para microabrasão propiciou diferenças na micromorfologia do esmalte de dentes decíduos.

Microinfiltração em dentes decíduos restaurados com resina composta após fotopolimerização com arco de plasma / Microleakage in primary teeth restored with resin composite using plasma arc photopolymerization

Introdução - O propósito deste estudo in vitro foi avaliar a microinfiltração em preparos ocluso-proximais em dentes decíduos restaurados com resina composta após fotopolimerização convencional ou com arco de plasma. Material e métodos - Foram utilizados dez molares decíduos, onde foram confeccionados preparos ocluso-proximais restaurados com resina composta fotopolomerizada por lâmpada convencional ou arco de plasma. As amostras foram divididas em dois grupos: G1 (n=10) fotopolimerização convencional e G2 (n=10) fotopolimerização com arco de plasma. Os espécimes foram termociclados, impermeabilizados, e imersos em corante. Após, foram seccionados e avaliados quanto à microinfiltração. Resultados - Os resultados obtidos demostraram que a fotopolimerização com arco de plasma diminuiu os níveis de microinfiltração. A análise estatística (teste de Mann-Whitney, p=0,002) indicou haver diferença significativa entre os grupos. Conclusão - Conclui-se que a fotopolimerização por arco de plasma diminuiu a microinfiltração em dentes decíduos restaurados com resina composta.

Microinfiltração sob diferentes tipos de selantes oclusais / Microleakge under different types of pit and fissure sealants

Foram selecionados quarenta pré-molares, divididos em quatro grupos de acordo com o selante aplicado: G1 - Delton; G2 - Conseal F; G3 - Fluroshield; G4 - Vitro Seal Alpha. Todos os espécimes foram termociclados, parcialmente impermeabilizados e armazenados em corante. Cada amostra foi seccionada longitudinalmente para análise da microinfiltração. Os resultados demonstraram que o selante Delton apresentou valores de microinfiltração significantemente maiores do que aqueles encontrados nos selantes Conseal F, Fluroshield e Vitro Seal Alpha (teste de Kruskal-Wallis, p>0.065). Concluiu-se que os selantes Conseal F, Fluoshield e Vitro Seal Alpha foram superiores ao selante Delton quanto à microinfiltração

Morfologia do esmalte dentário decíduo condicionado por diferentes agentes: estudo ao microscópio eletrônico de varredura / Morphology of primary tooth enamel etched by different agents: a scanning electron microscopy study

Observar in vitro, ao microscópio eletrônico devarredura, a micromorfologia do esmalte intacto de dentesdecíduos após o emprego de diferentes agentescondicionadores. Método: Foram selecionados 30 molaresdecíduos, clinicamente hígidos, que tiveram o terço médio dassuperfícies vestibulares condicionados por três diferentesagentes condicionadores. No G1 (n=10) foi aplicado a ácidofosfórico a 35 porcento durante 15s. No G2 (n=10) foi aplicado osistema adesivo autocondicionante de etapa única One-upBond F. No G3 (n=10) o condicionamento ácido foi realizadocom a aplicação do primer do sistema adesivoautocondicionante de duas etapas Clearfil SE Bond. Após osdiferentes tratamentos, todas as amostras foram desidratadas,montadas em bases metálicas, cobertas com ouro eobservadas ao microscópio eletrônico de varredura Jeol JSM6.100. Resultados: A análise das eletromicrografias revelouque as amostras do G1 apresentaram a formação de inúmerasmicroporosidades bem evidentes, classificadas como padrãoTipo 1 de Silverstone et al. (1975). As amostras do G2apresentaram um padrão predominantemente Tipo 2, porémmenos evidentes do que nas amostras do G1. Já nas amostrasdo G3 não foi observado um padrão de condicionamentodefinido. Conclusão: A utilização de diferentes agentescondicionadores resultou na formação de padrões decondicionamento ácido variados, na superfície do esmaltedecíduo

Microinfiltração em dentes decíduos restaurados com ionômero de vidro após preparo cavitário com Laser de ER: YAG / Microleakage in primary teeth restored with glass ionomer cement after Er: YAG laser cavity preparation

Objetivou-se avaliar a microinfiltração em restaurações classe V de cimento de ionômero de vidro modificado por resina (civ-mr) em dentes decíduos preparados com o laser de Er:YAG ou com instrumento cortante rotatório diamantado (ICRD). Foram utilizados 20 dentes decíduos anteriores. As restaurações foram realizadas com civ-mr. A seguir, os espécimes foram termociclados, impermeabilizados, imersos em corante, seccionados e avaliados. As amostras preparadas com o laser de Er:YAG apresentaram valores de microinfiltração significantemente menores do que as preparadas com ICRD (teste de Mann-Whitney, p = 0,003). Concluiu-se que o uso do laser de Er:YAG propiciou restaurações com menores graus de microinfiltração do que os das preparadas pelo método convencional.

O ensino dos procedimentos restauradores em molares decíduos nos cursos de Odontologia no Brasil / The teaching of primary molares restorative procedures in brazilian dental schools

O objetivo deste estudo foi avaliar as condutas de tratamento restaurador em molares decíduos adotados pelas disciplinas de Odontopediatria, nos diversos cursos de Odontologia existentes no Brasil. Foi enviado um questionário para a disciplina de Odontopediatria de103 cursos de odontologia, nas diversas regiões do país. Este averiguou dados sobre materiais forradores e restauradores "provisórios" e "definitivos" em preparos cavitários oclusais e ocluso-proximais de molares decíduos. Foram devolvidos 57 questionários respondidos (55,3 porcento do total). Os resultados demonstraram que em cavidades rasa houve uma predominância nanão indicação de forramento (69,64 porcento ocluso-proximais). Em cavidades médias, o forramento mais indicado foi o cimento de ionômero de vidro (CIV) em 35,72 porcento para as cavidades oclusais, e em 37,28 porcento para as ocluso/proximais. Nas cavidades profundas, a maior indicação foi para o hidróxido de cálcio + CIV em 70 porcento nas oclusais e em 70,17 porcento nas ocluso-proximais. Quanto aos materiais restauradores "provisórios" o CIV foi indicado em 71,21 porcento (oclusais) e 66,17 porcento (ocluso-proximais). Para as restaurações oclusais "definitivas", a resina composta híbrida foi indicada em 32,60 porcento. Nas restaurações ocluso-proximais "definitivas" indicou-se a resina composta híbrida em 35,58 porcento. Conclui-se que existe uma grande diversidade na indicação de materiais forradores e restauradores tanta nas cavidades oclusais como ocluso-proximais de molares decíduos

Influência do sistema adesivo na microinfiltração em restaurações de compômeros em dentes decíduos / Influence of adhesive system on microleakage of compomer restorations in primary teeth

O objetivo deste estudo in vitro foi comparar a microinfiltração em restaurações classe V de dentes decíduos restaurados com compômero (Dyract AP/Dentsply), após a utilização de diferentes sistemas adesivos: Prime & Bond 2.1 (Dentsply) e Prompt L-Pop (ESPE). Foram selecionados vinte dentes decíduos anteriores que, após a confecção dos preparos cavitários, foram divididos em dois grupos: G1 (n=10), aplicação do Prime & Bond 2.1; G2 (n=10), aplicação do Prompt L-Pop. Todas as amostras foram restauradas com o Dyract AP, seguindo-se as recomendações do fabricante. A seguir foram termocicladas (500 ciclos - 5°C e 55°C - 30 segundo em cada banho) impermeabilizadas e imersas em azul de metileno a 0,5 por cento por 4 horas. Foram seccionadas e avaliadas quanto à microinfiltração através de escores. Os resultados demonstraram que as amostras do G1 apresentaram valores menores de microinfiltração. A análise estatística (teste de Mann-Whitney, p=0,002) indicou que a diferença foi significante. Concluiu-se que o uso do Prime & Bond 2.1 propiciou um melhor vedamento da interface dente-restauração

Effects of a non-rinse conditioner on the enamel of primary teeth

O objetivo deste estudo in vitro foi de avaliar ao microscópio eletrônico de varredura os aspectos morfológicos do esmalte de dentes decíduos após condicionamento com ácido fosfórico a 36 por cento ou com um agente condicionador não lavável. Foram selecionados 10 dentes decíduos anteriores esfoliados naturalmente. As amostras sofreram limpeza coronária com pasta de pedra-pomes e água, em baixa-velocidade. O condicionamento foi realizado no esmalte da face vestibular. Os espécimes foram divididos em dois grupos: G1 (n=10): condicionamento com ácido fosfórico a 36 por cento na forma de gel - Conditioner 36 (Dentsply) durante 20 segundos, seguidos de lavagem com água durante 15 segundos; G2 (n=10): condicionamento com NRC - Non Rinse Conditioner (Dentsply) durante 20 segundos, seguidos de secagem com ar durante 15 segundos. As amostras foram desidratadas, montadas em bases metálicas e cobertas com ouro para análise ao microscópio eletrônico de varredura (Jeol JSM 6.100). A análise da eletromicrografias revelou que ambos os agentes condicionadores foram efetivos para condicionar o esmalte de dentes decíduos, causando microporosidades mas com melhor resultado quando utilizou-se o ácido fosfórico a 36 por cento na forma de gel.